Tile & Stone Installation
Floor and Wall Thin-Set Mortar (726/727)
SGM Floor and Wall Thin-Set Mortar is a premium Portland cement-based mortar specifically formulated for the installation of ceramic, mosaic, quarry tiles, and dimension stone (absorptive, semi-vitreous, and vitreous) tiles. This product can be used for service in commercial and residential environments for use on both wall and floor tile installations. It features a creamy consistency and extended open time over traditional dry-set mortars. SGM — Southcrete™ 28 Flexible Mortar Additive maximizes the performance of SGM Floor and Wall Thin-Set Mortar (726/727) resulting in a flexible and long-lasting bond specifically for glass tile installations. Meets ANSI 118.4 recommendations.
- Concrete and Plaster Surfaces: All floors should be twenty-eight (28) days cured and shall be structurally sound, clean,, and free of any moisture, wax, oil, paint particles, curing agents, or foreign matter. The slab should have a steel trowel or broom swept finish. Remove any liquid curing agents or concrete sealers, followed by a clear water wash. Surfaces may be cleaned with sulfamic acid (SGM Safe Clean Crystals) then thoroughly flushed and neutralized. Concrete shall be free of any efflorescence and hydrostatic pressure. Test to confirm that concrete can absorb water by sprinkling water droplets. If water beads up and does not absorb into substrate, scarify surface via mechanical abrasion with a Carborundum disk followed by a clear water wash. Test again to ensure that water is absorbed into substrate before proceeding with installation. Smooth concrete should also be roughened to ensure a mechanical bond. For hot and dry conditions, lightly dampen surface with water, leaving no standing water.
- Plywood And Wooden Substrates: All plywood floors (including subfloors) shall be engineered to meet all ANSI requirements. All plywood shall be an exterior grade (for interior, residential, and light commercial use in dry areas only), free of dust, oil, or other foreign matter. SGM Floor and Wall Thin-Set Mortar (726/727) shall be mixed with Southcrete™ 25 Acrylic or Southcrete™ 28 Flexible Additive in lieu of mixing water when installing tiles over these substrates.
- Alternate Surfaces: To bond over existing ceramic tile, marble, vinyl, VCT, and resilient flooring, floors must be bonded well to its subfloor and free of any wax, oil, dust, or paint particles. For use over existing ceramic tile, scarify surface of tile via mechanical abrasion with a Carborundum disk followed by a clear water wash. Do not use over wood, vinyl, particleboard, luan plywood, gypsum-based underlayments, wall coverings, adhesive residue, masonite, metal, glass, plastic, or painted surfaces.
Surfaces such as these will prevent bonding and should be covered with a cleavage membrane topped with a ? inch to ¾ inch (9.5 to 19.1 mm) reinforced mortar bed for floors. Wait a minimum of twenty (20) hours before dryset mortar may be applied to the mortar bed. Not recommended for setting green or black marble, vitreous or impervious tile (i.e. porcelain tile). Use Southcrete™ 25 Acrylic or Southcrete™ 28 Flexible Additive in lieu of mixing water when installing a vitreous or impervious (porcelain) tile. Green and black moisture-sensitive marble must be set with SGM EGS Epoxy Mortar. Consult SGM technical service department for product and installation recommendations.
- Expansion Joints: Do not tile over expansion, cold, or control joints. Follow the Tile Council of North America (TCNA) Handbook 2019, Method EJ 171 for detailed specifications.
WARNING — EYE IRRITANT CONTAINS PORTLAND CEMENT. Product is alkaline on contact with water. Use paddle for mixing to avoid splashing into eyes or contact with skin. During mixing or application avoid contact with eyes. In case of such contact, flood eyes repeatedly with water and CALL A PHYSICIAN. Wash thoroughly after handling and before smoking or eating. Do not take internally. CONTAINS FREE SILICA — DO NOT BREATHE DUST. Prolonged exposure to dust may cause delayed lung disease (Silicosis). WARNING: This product may expose you to chemicals, including silica, which the State of California recognizes as a cause of cancer. For more information, visit the Proposition 65 Warnings Website (www.P65Warnings.ca.gov). Use NIOSH approved masks at all times to handle silica dust. KEEP OUT OF REACH OF CHILDREN.
Add SGM Floor and Wall Thin-Set Mortar (726/727) powder to approximately 1 ½ gal (5.7 L) cool, clean potable water, Southcrete 25 Acrylic or Southcrete 28 Flexible Additive per 50lb (22.7Kg) bag. Machine mixing with a slow speed drill and mixing paddle is preferred (250-350 RPM). Higher speeds are not recommended and will entrain air. Mix the two components together thoroughly until smooth. The proper consistency is obtained when the mortar is applied with the notched trowel to the substrate and the ridges formed do not flow or slump. Allow mortar to slake for 5 minutes, and then remix before use. Do not add any additional water, latex or powder after the mortar has slaked. Re-mix mortar occasionally during use and discard after initial set in bucket.
Detailed installation procedures may be found in TCNA Handbook and ANSI 108.5. All materials and effected areas should remain above 50°F / 10°C (fifty degrees Fahrenheit / ten degrees Celsius) or below 100°F / 38°C (100 degrees Fahrenheit / 38 degrees Celsius) 24-hours prior and 72-hours after placement. Apply mixed mortar liberally with the flat side of trowel, using sufficient pressure to key into substrate, then apply additional mortar with notched edge of trowel leaving enough mortar to give 100 percent coverage with the back of tile. Place tile while surface is wet and tacky and spread mortar over an area no greater than can be covered with tile before the mortar skins over. Place tiles with a twisting motion and beat lightly before initial set takes place to fully embed in the mortar. Mortar that has formed a skin should be re-troweled before applying tile. Some irregular tiles may require back-buttering. During the setting of tile, it is recommended to periodically remove a tile and check to see that sufficient transfer of mortar is being attained. Industry standards require a minimum of 3/32 inch (2 mm) mortar thickness after beat in. Do not adjust tiles after they have been set more than ten (10) to fifteen (15) minutes.
- NOTE: It is suggested that a mock-up for the evaluation of surface preparation techniques and application be done by applying three (3) to four (4) tiles and bonding mortar from the actual installation. These tiles should be left to cure for three (3) to seven (7) days and then removed to determine if an adequate bond has been obtain before commencement of the installation.
A ¼ inch gap shall be left around vertical abutments to allow for structural movement and filled with appropriate Elastomeric sealant.
Use water to remove uncured mortar. Remove excess mortar from both glass block and tools before mortar hardens. Use of damp clean sponge or soft cloth is recommended.
Minimum cure is reached in 48-72 hours. Curing may vary according to atmospheric conditions.
- 75 sq. ft. per 50 lbs. when applied with ¼” x ¼” (6.4 mm x 6.4 mm) sq. notched trowel.
- 65 sq. ft using ¼” x ?” (6.4 mm x 9.5 mm) sq. notched trowel.
- 40 sq. ft. using ½” x ½” (13 mm x 13 mm).
Up to one (1) year from date of manufacture in an unopened, properly stored container.
SGM Inc. warrants this product will perform in accordance with its intended use for a period of one year from the date of manufacture. Any claim for defective products must be submitted in writing to SGM Inc. and samples of the defect must be provided. SGM Inc. ‘s sole obligation will be to replace any product determined to be defective by SGM Inc. EXCEPT AS PROVIDED HEREIN, SGM INC. MAKES NO OTHER REPRESENTATION OR WARRANTY OF ANY KIND, INCLUDING ANY WARRANTY OF MERCHANTABILITY OR FITNESS FOR PARTICULAR PURPOSE. IN NO EVENT SHALL SGM INC. BE LIABLE FOR DAMAGES OF ANY KIND OR NATURE, WHETHER ARISING BY CONTRACT, TORT OR OTHERWISE. SGM INC.’S SOLE OBLIGATION WILL BE TO REPLACE ANY PRODUCT DETERMINED BY SGM INC. TO BE DEFECTIVE.